  1. Which one is NOT an agglomeration process?
  2. A.
    Nodulizing
    B.
    Briquetting
    C.
    Roasting
    D.
    Pelletizing

    View Answer

    Workspace

    Discuss Discuss in Forum


  3. During LD blow in steelmaking the impurity that gets removed first is
  4. A.
    Carbon
    B.
    Phosphorous
    C.
    Manganese
    D.
    Silicon

    View Answer

    Workspace

    Discuss Discuss in Forum


  5. During the solidification of a pure metal, it was found that dendrites are formed. Assuming that the liquid-solid interface is at the melting temperature, the temperature from the interface into the liquid
  6. A.
    Decreases
    B.
    Increases
    C.
    Remains constant
    D.
    Increases and then decreases

    View Answer

    Workspace

    Discuss Discuss in Forum


  7. A peak in the X-ray diffraction pattern is observed at 2θ = 78o, corresponding to {311} planes of an fcc metal, when the incident beam has a wavelength of 0.154 nm. The lattice parameter of the metal is approximately
  8. A.
    0.6 nm
    B.
    0.4 nm
    C.
    0.3 nm
    D.
    0.2 nm

    View Answer

    Workspace

    Discuss Discuss in Forum


  9. If d is the inter-planar spacing of the planes {h k l}, the inter-planar spacing of the planes {nh nk nl}, n being an integer, is
  10. A.
    d
    B.
    d/n
    C.
    nd
    D.
    d/n2

    View Answer

    Workspace

    Discuss Discuss in Forum


  11. As temperature increases, the electrical resistivities of pure metals (ρm) and intrinsic semiconductors (ρs) vary as follows
  12. A.
    Both ρm and ρs increase
    B.
    Both ρm and ρs decrease
    C.
    ρm increases and and ρs decreases
    D.
    ρm decreases and and ρs increases

    View Answer

    Workspace

    Discuss Discuss in Forum


  13. At equilibrium spacing in a crystalline solid, which of the following is true for net inter-atomic force (F) and potential energy (U)
  14. A.
    F is zero and U is zero
    B.
    F is zero and U is minimum
    C.
    F is minimum and U is zero
    D.
    F is minimum and U is minimum

    View Answer

    Workspace

    Discuss Discuss in Forum


  15. The property of a material that CANNOT be significantly changed by heat treatment is
  16. A.
    Yield strength
    B.
    Ultimate tensile strength
    C.
    Ductility
    D.
    Elastic modulus

    View Answer

    Workspace

    Discuss Discuss in Forum


  17. A unit dislocation splits into two partial dislocations. The correct combination of the Burgers vectors of the partial dislocations for a given unit dislocation having Burgers vector  is
  18. A.
    .

    B.
    .

    C.
    .

    D.
    .

    View Answer

    Workspace

    Discuss Discuss in Forum


  19. A polymer matrix composite is reinforced with long continuous ceramic fibres aligned in one direction. The Young's moduli of the matrix and fibres are Em and Ef respectively, and the volume fraction of the fibres is f. Assuming iso-stress condition, Young's modulus of the composite EC in a direction perpendicular to the length of fibres, is given by the expression
  20. A.
    EC = (1 - f)Em + fEf
    B.
    EC = (1 - f)Ef + fEm
    C.
    1/EC = (1 - f)/Em + f/Ef
    D.
    1/EC = (1 - f)/Ef + f/Em

    View Answer